控制块的阻力

块电阻如何控制?

块电阻的倾向另一个表面涂层不遵守。例如,当一个部分是画和包装用纸,纸可能坚持“干油漆。”This is an example of poor block resistance. If the paint is fully dry and not able to flow, block resistance is usually good. Crosslink density improves block resistance. In lacquer systems, the solvent evaporation is the key to block resistance. This solvent includes coalescent aids and many volatile additives. Usually paints will have an increase in glass transition temperature or hardness with time. Use of more volatile, faster evaporating, solvents may help. In addition, additives that reduce adhesion, such as silicones and fluorocarbon additives, may help. Other additives, such as some extender pigments and polyethylene or polypropylene additives, may reduce block adhesion problems. Experimentation will be needed to find what works best in your case. Remember, most additives have multiple effects. Be careful that an additive does not create a bigger problem.

Dual-Cure紫外线技术

什么dual-cure技术用于UV -治疗系统?

在根治方法紫外线系统中,过氧化物可用于一些系统热治疗经过紫外线系统。Moisture-cure聚氨酯化学还可以用于从根本上治愈系统。在阳离子系统中,热诱导阳离子化学可以治愈环氧系统结合使用。双重治疗技术通常使用的网站是不可能的。例如,在色泽鲜艳的涂料、厚涂料或基质的孔隙度不允许的网站。

DTM涂层附着力的因素

什么因素会影响附着力的DTM(直接金属)涂料吗?

direct-to-metal涂料的附着力等添加剂可以改变表面活性剂,去沫剂、润湿艾滋病,和分散剂通常是一个负面意义。表面的清洁是非常重要的今天使用的高固体DTM涂料。没有溶剂溶解油脂和污垢表面上,DTM通常会比旧的低性能降低这些表面固体版本。添加剂放入DTM涂料如硅烷偶联剂也将有助于在干净的底物,但他们对污染的表面是非常无效的。我们在实验室做一个出色的表面准备,但在现实世界中有更多的石油和其他表面污染物。所有的评估都应该在真实的样本,而不仅仅是在原始实验室优惠券。

在UV固化丙烯酸酯与丙烯酸甲酯

为什么丙烯酸酯和丙烯酸甲酯用于大多数uv固化涂料吗?

都是使用和可以用来制造优秀的涂料。接受根治方法,但激进的链增长的丙烯酸甲酯更稳定,从而有更多的时间与氧气反应,其分子量缩短。因此,丙烯酸甲酯需要毯子的氮涂料降低氧浓度。在这样做时,丙烯酸甲酯的工作。丙烯酸酯不需要氮气的毯子。然而,丙烯酸酯将产生更好的电影如果他们治愈下氮气层。在这两种情况下,涂层的表面会有更多与氧气反应,导致表面性质不同的涂层更深层的电影。在某些情况下,这个可怜的表面治疗很容易导致了涂层或表面似乎油性。

运营商减少偏差

运营商之间的偏差应该我们通常看到多少经费?

任何涉及到人类的方法可以产生错误。我们发现,对于一个给定的撤军酒吧1 - 3%的膜厚度变化是典型的如果他们都以类似的方式做这件事。然而,如果不是标准化的方法可以更大的错误。还可以有错误由于使用不同的撤军酒吧。通常这只是1到10%,这取决于厚度。如果使用多个撤军酒吧,一些可以找到最相似的,检查其使用指定。陈旧的酒吧应该重组或替换。